Abstract & Overview
The heat treatable aluminum–copper alloy AA2014 finds wide application in the aerospace and defence industry due to its high strength-to-weight ratio and good ductility. Friction stir welding (FSW) process, an emerging solid state joining process, is suitable for joining this alloy compared to fusion welding processes. This work presents the formulation of a mathematical model with process parameters and tool geometry to predict the responses of friction stir welds of AA 2014-T6 aluminum alloy, viz yield strength, tensile strength and ductility. The most influential process parameters considered are spindle speed, welding speed, tilt angle and tool pin profile. A four-factor, five-level central composite design was used and a response surface methodology (RSM) was employed to develop the regression models to predict the responses. The mechanical properties, such as yield strength (YS), ultimate tensile strength (UTS) and percentage elongation (%El), are considered as responses. Method of analysis of variance was used to determine the important process parameters that affect the responses. Validation trials were carried out to validate these results. These results indicate that the friction stir welds of AA 2014-T6 aluminum alloy welded with hexagonal tool pin profile have the highest tensile strength and elongation, whereas the joints fabricated with conical tool pin profile have the lowest tensile strength and elongation.